ZOU YuGang, LIU Jie, ZHANG Xing, JIANG Yan, HU JinSong, WAN LiJun
Sci. China Chem. , 2014, 57(11):1552-1558
Abstract (click image for pdf file)
The kesterite Cu2ZnSn(S,Se)4 (CZTSSe) is an ideal candidate for light harvesting materials in earth-abundant low-cost thin-film solar cells (TFSC). Although the solution-based processing is a most promising approach to achieve low-cost solar cells with high power conversion efficiency, the issues of poor crystallinity and carbon residue in CZTSSe thin films are still challenging. Herein, a non-hydrazine solution-based method was reported to fabricate highly crystallized and carbon-free kesterite CZTSSe thin films. Interestingly, it was found that the synthetic atmosphere of metal organic precursors have a dramatic impact on the morphology and crystallinity of CZTSSe films. By optimizing the processing parameters, we are able to obtain a kesterite CZTSSe film composed of compact large crystal grains with trace carbon residues. Also, a viable reactive ion etching (RIE) processing with optimized etching conditions was then developed to successfully eliminate trace carbon residues on the surface of the CZTSSe film. 